| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | mtc-m16d.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 8JMKD3MGP7W/36HQ6QE |
| Repositório | sid.inpe.br/mtc-m19@80/2009/12.10.15.38 (acesso restrito) |
| Última Atualização | 2009:12.10.15.38.08 (UTC) administrator |
| Repositório de Metadados | sid.inpe.br/mtc-m19@80/2009/12.10.15.38.09 |
| Última Atualização dos Metadados | 2018:06.05.04.36.01 (UTC) administrator |
| Chave Secundária | INPE--PRE/ |
| DOI | 10.1016/j.apsusc.2009.09.001 |
| ISSN | 0169-4332 |
| Chave de Citação | MelloUedaLepiReut:2009:TrChSS |
| Título | Tribological changes on SS304 stainless steel induced by nitrogen plasma immersion ion implantation with and without auxiliary heating  |
| Ano | 2009 |
| Mês | Dec. |
| Data de Acesso | 04 maio 2024 |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 375 KiB |
| 2. Contextualização | |
| Autor | 1 Mello, Carina Barros 2 Ueda, Mário 3 Lepienski, C. M. 4 Reuther, H. |
| Identificador de Curriculo | 1 2 8JMKD3MGP5W/3C9JHSB |
| Grupo | 1 LAP-CTE-INPE-MCT-BR 2 LAP-CTE-INPE-MCT-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Universidade Federal do Paraná 4 Institute of Ion Beam Physics and Materials Research |
| Revista | Applied Surface Science |
| Volume | 256 |
| Número | 5 |
| Páginas | 1461-1465 |
| Nota Secundária | B2_ASTRONOMIA_/_FÍSICA B2_CIÊNCIAS_BIOLÓGICAS_I B2_CIÊNCIAS_BIOLÓGICAS_II B1_ECOLOGIA_E_MEIO_AMBIENTE B1_ENGENHARIAS_II A2_ENGENHARIAS_III B1_ENGENHARIAS_IV A2_INTERDISCIPLINAR B2_MATEMÁTICA_/_PROBABILIDADE_E_ESTATÍSTICA B1_MATERIAIS B1_MEDICINA_III B1_ODONTOLOGIA B3_QUÍMICA |
| Histórico (UTC) | 2009-12-10 15:38:41 :: simone -> administrator :: 2018-06-05 04:36:01 :: administrator -> marciana :: 2009 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Palavras-Chave | Plasma immersion ion implantation SS304 Tribology |
| Resumo | In order to achieve quite thick treated layers with reasonable thickness uniformity in SS304 steel, the plasma immersion ion implantation (PIII) process was run in high-temperature, up to 350 °C, to induce high thermal diffusion but avoid the white layer formation. In these experiments, we heated the sample-holder with a shielded resistive wire properly wound around it and subjected the SS samples to nitrogen glow discharge PIII with relatively low voltages (10 kV) in different temperatures. We also treated the SS samples by the traditional PIII method, slowly increasing the high voltage pulse intensities, until 14 kV at the end of processing, reaching temperatures of up to 350 °C. These modes of treatments were compared with respect to nitrogen implantation profiles, X-ray diffraction, tribology and mechanical properties. X-ray diffraction results indicated a much higher efficiency of auxiliary heated PIII mode compared to the ordinary PIII. Very prominent ãN peaks were observed for the first mode, indicating large concentration of nitrogen in thick layers, confirmed by the nitrogen profiles measured by GDOS and AES. Improved mechanical and tribological properties were obtained for SS304 samples treated by the PIII with auxiliary heating, more than for ordinary PIII. Hardness was enhanced by up to 2.77 times, as seen by nanoindentation tests. |
| Área | FISPLASMA |
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Tribological changes on... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | tribological changes.pdf |
| Grupo de Usuários | administrator simone |
| Visibilidade | shown |
| Política de Arquivamento | denypublisher denyfinaldraft24 |
| Permissão de Leitura | deny from all and allow from 150.163 |
| 5. Fontes relacionadas | |
| Repositório Espelho | sid.inpe.br/mtc-m19@80/2009/08.21.17.02.53 |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS |
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX. |
| Acervo Hospedeiro | sid.inpe.br/mtc-m19@80/2009/08.21.17.02 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel documentstage e-mailaddress electronicmailaddress format isbn label lineage mark nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project readergroup rightsholder schedulinginformation secondarydate session shorttitle sponsor subject tertiarymark tertiarytype typeofwork url versiontype |
| 7. Controle da descrição | |
| e-Mail (login) | marciana |
| atualizar | |